Altintas, ASarigün, YÇavdar, U2024-07-182024-07-180034-85701988-4222http://akademikarsiv.cbu.edu.tr:4000/handle/123456789/4410Ekabor 2 powder of different weights, used by V type powder mixture was mixed with pure iron powder. Specimens were created by dry pressing into die followed by cold isostatic press at a pressure of 100 bar for purpose of resizing. The conventional sintering process at 900 degrees C and 950 degrees C was carried out for 4 h using conventional furnaces. Specimens were gradually cooled by air. The sintered pellets were examined in terms of density, wear abrasion, surface roughness and hardness at 900 degrees C and 950 degrees C. Microstructure of pellets was observed with optic microscope. The results show that the hardness gradually increased with additions of 0 wt. % to 10 wt. % of Ekabor 2 however, after 10 wt. %, this hardness tended to decrease.EnglishKINETICSSTEELCERAMICSArticle