Burak GÜLLevent Ulvi GEZİCİMehmet AYVAZUğur ÇAVDAR2024-07-242024-07-242020http://akademikarsiv.cbu.edu.tr:4000/handle/123456789/25729In this study, compressibility, and conventional and ultra-high frequency induction sinteringbehaviors of 99.8% purity and 50-70 µm size range aluminum powders were investigated. In thecompressibility studies, uniaxial-cold pressing method was used. Green samples were produced inthe range of 50-275 MPa using different pressures. By measuring the apparent densities of theproduced samples, the optimum compressibility pressure was determined as 200 MPa. Purealuminum powder metal samples produced with this ideal pressing pressure were sintered in bothclassical and ultra-high frequency induction methods in the range of 500-600 oC. Sintering wasperformed as 40 min in the traditional method and 5 min in the ultra-high frequency inductionsintering method. As a result of the tests carried out in this study, it was determined that purealuminum samples were successfully sintered with a high frequency induction system in a shortertime than traditional sintering method.engAraştırma Makalesi10.35860/iarej.729395