    Effect of constraint on fracture behavior of welded 17mn4 and aisi304 steels
    Uyulgan, B; Cetinel, H; Aksoy, T
    In this study, 17Mn4 (P295GH) pressure vessels steel and AISI304 stainless steel were welded with ER309L austenitic consumable. In experimental part of the study, tensile tests were conducted on welded plates and variation of hardness values along specimen was measured. J-integral fracture toughness values were investigated for different crack locations. In order to determine the regions where plastic deformation did not take place due to constraint, uni-axial tensile test was performed on welded tensile specimen after attaching strain gauges. In numerical part of the study, finite element (FE) analyses were conducted by fixing 2-D models precracked on different locations by using ANSYS software. In these models, stress triaxiality and plastic deformation characteristics around crack tip were determined for each crack locations after stress - strain analyses. The limitation on the extension of plastic deformation at diffusion line causes extra increase in stress triaxiality at crack tip.
  • No Thumbnail Available
    Item
    Fracture behavior of various welded steels
    Ozdemir, TE; Cetinel, H; Uyulgan, B
    In this study, P295GH (17Mn4) pressure vessel steel and AISI 304 stainless steel were joined by using ER 309L electrodes. Welded specimens were fatigued by four point bending experiments. Cracks occurred on the stainless steel side of the weldment during the fatigue tests. Finite element (FE) analyses were conducted by fixing 2-D precracked model for welded 17Mn4 pressure vessel steel and AISI 304 stainless steel by using ER 309L electrodes. True stress and true strain values of the AISI 304, 17Mn4 steels and ER 309L electrodes were determined by tensile tests. Stress analyses were conducted after entering the linear and nonlinear properties of the materials into software manually. Eventually, fracture mechanics analyses were conducted for the model, and J integral fracture toughness values of the crack on the weldment were calculated.