Microstructural and Radioluminescence Characteristics of Nd3+ Doped Columbite-Type SrNb2O6 Phosphor

Simple item page
dc.contributor.authorEkmekçi, MK
dc.contributor.authorIlhan, M
dc.contributor.authorEge, A
dc.contributor.authorAyvacikli, M
dc.date.accessioned2025-04-10T10:30:24Z
dc.date.available2025-04-10T10:30:24Z
dc.description.abstractUndoped and different concentration Nd3+ doped SrNb2O6 powders with columbite structure were synthesized by molten salt process using a mixture of strontium nitrate and niobium (V) oxide and NaCl-KCl salt mixture as a flux under relatively low calcining temperature. X-ray diffraction analysis results indicated that SrNb2O6 phases found to be orthorhombic columbite single phase for undoped, 0.5 and 3 mol% Nd3+ doping concentrations. Phase composition of the powders was examined by SEM-EDS analyses. Radioluminescence properties of Nd3+ doped samples from UV to near-IR spectral region were studied. The emissions increased with the doping concentration of up to 3 mol%, and then decreased due to concentration quenching effect. There is a sharp emission peak around 880 nm associated with F-4(5/2) -> I-4(9/2) transition in the Nd3+ ion between 300 and 1100 nm. The broad emission band intensity was observed from 400 to 650 nm where the peak intensities increased by increasing Nd3+ doping concentration. All the measurements were taken under the room temperature.
dc.identifier.e-issn1573-4994
dc.identifier.issn1053-0509
dc.identifier.urihttp://hdl.handle.net/20.500.14701/37010
dc.language.isoEnglish
dc.titleMicrostructural and Radioluminescence Characteristics of Nd3+ Doped Columbite-Type SrNb2O6 Phosphor
dc.typeArticle