Structural and tunable optical properties of LiMgPO4:Tb3+ phosphor fabricated by sol–gel method
No Thumbnail Available
Date
2024
Authors
Journal Title
Journal ISSN
Volume Title
Publisher
Abstract
In the study, Tb3+-doped LiMgPO4 phosphors between.10 and 5 mol% were successfully synthesized by the sol–gel process. The crystal structure of Tb3+-doped LiMgPO4 was identified by X-ray diffraction (XRD), scanning electron microscopy (SEM), and X-ray photoelectron spectroscopy (XPS) analyses. The XRD results for LiMgPO4 ceramics doped with Tb3+ indicated a single-phase up to 5 mol%, accompanied by lattice shrinkage. An SEM analysis of LiMgPO4 samples showed that increasing Tb3+ concentration reduced grain size but did not cause any significant change in slightly angular and round grains. The emission intensity of phosphor increased from.10 to 5 mol%, and no concentration quenching was observed. The luminescence color of LiMgPO4:Tb3+ phosphor can be tuned from blue to green through cross-relaxation with the increase in Tb3+ concentration. The photoluminescence emissions of LiMgPO4:Tb3+ on the CIE diagram shifted from blue to green as the Tb3+ concentration increased. The color purity of the 5 mol% Tb3+-doped phosphor showing the strongest emission was measured at 22.71%, whereas the color-correlated temperature parameter was found to be 5573 K. The phosphors exhibited bi-exponential decay profiles, and the observed lifetimes of 5D3 decreased with the increase of Tb3+, where the cross-relaxation effect increased. The quantum efficiency (ɳQE) of the phosphor was determined using the cross-relaxation process. For Tb3+ concentrations ranging from.1 to 5 mol%, the ɳQE of the 5D3 state decreased from 62.49% to 28.29%. The research may offer a new perspective and new approaches for tuning luminescence in Tb3+-doped phosphors. © 2024 The Authors. International Journal of Applied Ceramic Technology published by Wiley Periodicals LLC on behalf of American Ceramics Society.
Description
Keywords
Color , Crystal structure , Luminescence , Magnesium compounds , Scanning electron microscopy , Sols , Terbium compounds , X ray diffraction , X ray photoelectron spectroscopy , Color-tunable , Color-tunable phosphor , Crossrelaxation , Crystals structures , Decay time , Sol- gel methods , Synthesised , Tb3+ doping , Tunable optical properties , X- ray diffractions , Phosphors