Effect of production parameters on wear behavior in Al/SiCp composites produced by the P/M method; [T/M yöntemi ile üretilmiş Al-SiC p kompozitlerde üretim parametrelerinin aşinma davranişina etkisi]

Simple item page
dc.contributor.authorŞahin S.
dc.contributor.authorÖzdemir I.
dc.contributor.authorÜnlü B.S.
dc.date.accessioned2024-07-22T08:25:14Z
dc.date.available2024-07-22T08:25:14Z
dc.date.issued2002
dc.description.abstractIn this study, Al based composites reinforced with SiCp were produced by the P/M method. In manufactured composites proportions of reinforced SiCp were chosen to be 5%, 10%, 15% and 20% by weight. Experimental sample of Al/SiCp composites which are 35mm in diameter and 10mm in lenght were pressed at pressures of 500MPa and 350MPa and the composites were sintered an argon gas environment at 600°Cfor period of 30 min. Density and hardness test of produced composites were performed their wesr behaviours were investigated. Wear test were carried out using a pin-on disc type tribometer with rubbing against 600 grit SiC abrasive paper. It was observed that the increase of compression pressure and reinforing fraction improved wear resistance of the composites.
dc.identifier.urihttp://akademikarsiv.cbu.edu.tr:4000/handle/123456789/20329
dc.language.isoTurkish
dc.subjectArgon
dc.subjectHardness testing
dc.subjectPowder metallurgy
dc.subjectSilicon compounds
dc.subjectSintering
dc.subjectWear of materials
dc.subjectWear resistance
dc.subjectAl/SiC composites
dc.subjectCompression pressure
dc.subjectProduction parameters
dc.subjectComposite materials
dc.titleEffect of production parameters on wear behavior in Al/SiCp composites produced by the P/M method; [T/M yöntemi ile üretilmiş Al-SiC p kompozitlerde üretim parametrelerinin aşinma davranişina etkisi]
dc.typeConference paper