In this study, modulus of rupture, elastic modulus and fracture toughness values were investigated at elevated temperature for magnesia and magnesia-chromite content of chromite between 6% and 20%. Modulus of rupture and elastic modulus values were calculated by three point bending test at temperatures 400, 600, 800 and 1400 degreesC. Modulus of rupture and Young's modulus values decreased when temperature and content of chromite increased. Modulus of rupture and Young's modulus values at room temperature were compared to the values at 400, 600, 800 and 1400 degreesC. Young's modulus values decreased to about 40% and modulus of rupture values decreased to about 25% of the values at room temperature. The samples were notched as a/h = 0.3 by cutting tool of 0.2 mm thickness. Fracture toughness values were calculated at each temperature. Fracture toughness value at room temperature was compared to the values at 400, 600, 800 and 1400 degreesC. It was seen that fracture toughness values had decreased by the increase at temperature.

URI

http://akademikarsiv.cbu.edu.tr:4000/handle/123456789/6507

Collections

Web of Science Koleksiyonu