Effect of production parameters on wear behavior in Al/SiCp composites produced by the P/M method; [T/M yöntemi ile üretilmiş Al-SiC p kompozitlerde üretim parametrelerinin aşinma davranişina etkisi]
| dc.contributor.author | Şahin S. | |
| dc.contributor.author | Özdemir I. | |
| dc.contributor.author | Ünlü B.S. | |
| dc.date.accessioned | 2025-04-10T11:18:03Z | |
| dc.date.available | 2025-04-10T11:18:03Z | |
| dc.date.issued | 2002 | |
| dc.description.abstract | In this study, Al based composites reinforced with SiCp were produced by the P/M method. In manufactured composites proportions of reinforced SiCp were chosen to be 5%, 10%, 15% and 20% by weight. Experimental sample of Al/SiCp composites which are 35mm in diameter and 10mm in lenght were pressed at pressures of 500MPa and 350MPa and the composites were sintered an argon gas environment at 600°Cfor period of 30 min. Density and hardness test of produced composites were performed their wesr behaviours were investigated. Wear test were carried out using a pin-on disc type tribometer with rubbing against 600 grit SiC abrasive paper. It was observed that the increase of compression pressure and reinforing fraction improved wear resistance of the composites. | |
| dc.identifier.uri | http://hdl.handle.net/20.500.14701/53154 | |
| dc.title | Effect of production parameters on wear behavior in Al/SiCp composites produced by the P/M method; [T/M yöntemi ile üretilmiş Al-SiC p kompozitlerde üretim parametrelerinin aşinma davranişina etkisi] | |
| dc.type | Conference paper |